公稱直徑
d

粗螺距P

dk

k

s

t
min

max

min

max

min

max

min

M1.4

0.3

2.74

2.46

1.4

1.26

1.36

1.32

0.6

M1.6

0.35

3.14

2.86

1.6

1.46

1.56

1.52

0.7

M2

0.4

3.98

3.62

2

1.86

1.56

1.52

1

M2.5

0.45

4.68

4.32

2.5

2.36

2.06

2.02

1.1

M3

0.5

5.68

5.32

3

2.86

2.58

2.52

1.3

M4

0.7

7.22

6.78

4

3.82

3.08

3.02

2

M5

0.8

8.72

8.28

5

4.82

4.095

4.02

2.5

M6

1

10.22

9.78

6

5.7

5.14

5.02

3

M8

1.25

13.27

12.73

8

7.64

6.14

6.02

4

M10

1.5

16.27

15.73

10

9.64

8.175

8.025

5

M12

1.75

18.27

17.73

12

11.57

10.18

10.025

6

M14

2

21.33

20.67

14

12.57

12.21

12.032

7

M16

2

24.33

23.67

16

15.57

14.21

14.032

8

M18

2.5

27.33

26.67

18

17.57

14.21

14.032

9

M20

2.5

30.33

19.67

20

19.48

17.23

17.05

10

M22

2.5

33.39

32.61

22

21.48

17.23

17.05

11

M24

3

36.36

35.61

24

23.48

19.28

19.065

12

M27

3

40.39

39.61

27

26.48

19.28

19.065

13.5

M30

3.5

45.39

44.61

30

29.48

22.28

22.065

15.6

組別

C

Si

Mn

P

S

Cr

Mo

Ni

Cu

特性

304-A2

0.1

1

2

0.05

0.03

15-20

8-19

4

加工硬化率適中，適于一般的冷間加工以及伸抽，冷加工性能較好，普遍用于外六角螺釘、螺母以及墊圈產(chǎn)品

316-A4

0.08

1

2

0.045

0.03

16-18.5

2-3

10-15

1

加鉬，耐腐蝕能力較304強，特別適用于海水及化學介質(zhì)，更加的耐腐蝕性及耐孔蝕性。

注：

1)如鎳含量低于8%,則錳的最小含量必須為5%
2)鎳含量大于8%時，對銅的最小含量不予限制
3)如鉻含量低于17%時，則鎳的最小含量為12%
4)對于最大含碳量0.03%的奧氏體不銹鋼，氮含量最高可達到0.22
5)對較大直徑的產(chǎn)品，為達到規(guī)定的機械性能，在制造者說明書中，可能有較高的含碳量，但對馬氏體鋼不應(yīng)超過0.12%

類別

組別

性能等級

螺絲直徑

抗拉強度mpa/mm²

規(guī)定非比列伸長應(yīng)為mpa/mm²

斷后伸長量mpa/mm²

奧氏體

A2，A4

50

≤ 39

500

210

0.6d

70

≤ 24

700

450

0.4d

80

≤ 24

800

600

0.3d